DiamonDyze™
is Mil 8625
compliant.
Salt Spray ASTM B 117: 2000 plus hours
and still in test.
*Accelerated Salt Spray: Over 3000 hrs,
cyclic, with no change in appearance.
(As of
5/1/2011)
*Humidity: Over 8000 hrs, cyclic, with
no change in appearance. (As of
5/1/2011)
Ford APGE cyclic corrosion test (FLTM B1
123-01): 80 cycles no effect on panels.
Test continuing.
Tabor Abrasive: 40,000 cycles and no
wear or weight loss.
**Chemical: A 24 hour soak in both an
Alcohol/MEK blend and Aircraft Stripper
(Contains Methylene chloride) shows no
effect.
**Oven Off: 12 hours no effect.
Thermal Resistance: DiamonDyze is
showing @ a 10% reduction in the rate of
thermal transfer (insulator).
Ra: Prior to Type II DiamonDyze the test
panel had a Ra of 2.791 (6061 aluminum
non polished) after DiamonDyze the same
panel had a Ra of 1.782.
Gravelometer: 5A
* Constant direct spray of a 5% salt
solution for 9 hours followed by 15
hours in the sealed test chamber with no
spray, followed by 9 hours of direct
spray. Repeated for 1 week, then the
chamber is kept sealed through the
weekend, experiencing
normal
temperature variations and spray is
resumed at the beginning of the next
week. This procedure has shown a
significant acceleration of oxidation
formation compared to
normal ASTM 117B conditions,
as it more closely mimics real world
exposure and allows for salt
accumulation on a part while no spraying
is occurring..
** DiamonDyze will not change the
resistance of a treated piece in certain
tests such as Nitric Acid testing. These
tests are directly impacted by other
treatments such as the seal used.
DiamonDyze will not negatively impact a
part as to chemical, corrosion or UV.
|